微蚀剂 SBT-203

一、 产品简介
I. Product Introduction

SBT-203作为H2SO4—H2O2系统波动剂对蚀刻波动结果精良,该蚀刻系统能匀称微蚀铜层外表,实用于孔金属化、图形电镀及镀金、镀镍前处置历程,别的还可用于挂具退铜。
As the stabilizing agent of H2SO4—H2O2system, SBT-203 has good stabilizing effect to etching. This etching system can evenly micro etch the copper layer surface. It can be used in the process before pore metalizing, pattern and gold plating, nickel plating as well as the copper stripping of hangers.

二、安装
II. Devices
载体/东西
Carrier/tool
材质要求
Material requirements
槽体材质
Material of tank body
硬质聚乙烯、聚丙烯
Rigid polyethylene, polypropylene

三、100升事情液配制
III.Preparation of 100 liters’ working solution
品名
Product Name
范畴
Scope
硬化水
De-mineralized water
约78升
About 78 liters
浓硫酸(98%)
Concentrated sulfuric acid(98%)
8升
8 liters
SBT-203 3升
3 liters
过氧化氢(30%)
Hydrogen peroxide (30%)
化学镀铜
Electro-less copper plating
8升
8 liters
  图形镀
Graphic plated copper
4升
4liters

四、工艺条件及控制目标
IV.Technical Conditions and Control Indicators
组份/参数
Components/parameters
最佳值/事情范畴/要求
Optimal value/working scope/requirement
事情温度
Working temperature
20-40℃
处置工夫    化学镀铜
Processing time  Electro-less copper plating
2-3分钟
2-3 minutes
图形铜
Graphiccopper
0.5-1分钟
0.5-1 minutes
H2O2 >6%
H2SO4 >8%
Cu2+ <80g/L

五、槽液维护
V.Maintenance of Solution

1. 每处置200Ft2补加浓硫酸0.5升,双氧水2升事情液,同时参加0.5升SBT-203(M101按双氧水补加量的20%补加),补加前应先舀出过量体积的事情液。
1. Add additional 0.5 liter of concentrated sulfuric acid, 2 liters of hydrogen peroxide working solution for each 200Ft2, meanwhile, add 0.5 liter of SBT-203(M101 added as per 20% of the additional hydrogen peroxide amount). Before additional adding, scoop out the right volume of the working solution.
2. 溶铜铜达80克/升事情液后需改换局部或所有槽液。
2. When the amount of dissolved copper comes up to 80 g / l liter’s working solution, part or all of the tank solution needs to be replaced.

六、剖析办法
VI.Analysis Methods

试样预备:取10.0ml粗化液于100ml的容量瓶中,加D.I水至刻度
Sampling preparation: put 10.0ml coarsening solution into a 100ml volumetric flask and then add D.I water to the scale.
硫酸
Sulphuric acid
1.汲取上述浓缩液20.0ml于250ml锥形瓶中,
1. Draw the above 20.0ml diluents from a 250ml conical flask,
2. 加100ml D.I.水,搅匀,加5滴甲基橙指示剂,
2. Add 100ml D.I. water, mix well and then add 5 drops of methyl orange indicator,
3.用0.1N NaOH滴定从白色到尽头桔黄色,
3. 0.1N NaOH is used to titrate to orange from red,
盘算: H2SO4 %(体积比)=13.3*(0.1N× NaOH斲丧ml )
Calculation: H2SO4 %(volume ratio)=13.3*(0.1N× NaOH consumption ml )

双氧水
Hydrogen peroxide

1. 汲取浓缩液20.0ml 250ml锥形瓶中,加100ml D.I.水,搅均,
1. Draw 20.0ml diluents from a 250ml conical flask, add 100ml D.I. water, and then mix well
2. 加40ml 20% H2SO4搅均,
2. Add 40ml 20% H2SO4, and mix well.
3. 用0.1N的KMnO4尺度液滴定至粉白色,
3. 0.1N KMnO4 standard solution is titrate to pink,
盘算: H2O2 %(体积比)=12.9×0.1×(尺度KMnO4斲丧ml )
Calculation:H2O2 %(volume ratio)=12.9×0.1×(Standard KMnO4 consumption ml )

铜含量
Cu content

1. 汲取浓缩液5.0ml于250ml锥形瓶中,加D.I水50ml,
1. Draw 5.0ml diluents from a 250ml conical flask, add 50ml D.I. water, and mix well
2. 加10ml 1:1的氨水,10ml的甲醇,3滴PAN指示剂,搅动,
2. Add 10ml 1:1 ammonia, 10ml methanol and 3 drops PAN indicator, and then mix them well
3. 用尺度0.10M EDTA滴定,直到颜色酿成淡绿色,
3. Standard 0.10M EDTA is used to titrate until it becomes pale green,

盘算: [Cu2+] g/L=(M.VEDTA)×63.54
Calculation: [Cu2+] g/L=(M.VEDTA)×63.54